Effect of Coaxing on the Fatigue StrengtJi of Spheroidal and Compacted Graphite Cast Iron

nasir kloub, A.R.I Kheder


In this research the effect of coaxing on the fatigue strength of

spheroidal and compacted graphite cast iron was studied. The stress-stress

cycle curves for both irons were established and the fatigue limits (6�v)

were deterrnined. They were 185 MPa for spheroidal graphite cast iron

(SGI) and 175 MPa for compacted graphite cast iron (CGI). Then

samples were subjected to two step loading; namely low-high loading.

The initial loading was 182 MPa for SGI which is lower than the        for

SGI by 3MPa and the initial loading was 172 MPa for CGI which is

lower than 6� for CGI by 3 MPa. For both irons the tests were run for

7x10*� cycles at the lower range of loading until the cracks started to

appear and stopped from growing, then specimens were subjected to

higher stresses; namely            220 MPa for SGI and 210 MPa for CGI until

failure of the specimens occurred. The results obtained for the coaxing

phenomenon in SGI showed 8.96 folds improvement and 7.34 folds for

CGI in fatigue life. The tests were done at room temperature at a stress

ratio of R= -I. The specimens were in form of strips which were

subjected to alternating bending fatigue test.