EVMiUATION OF ASPHAIiT MIXES DISINTEGEUV3JI0N CONTAIHING XNDUSTRIMi WASTES USING THE CANTABRO TEST

badreldeen amousa

Abstract


The industrial wastes prouduct need big areas to storage and how it is become

disposal problems. To reduce the susceptibilty of asphalt mixes to disintegration under

the effects of high stress, the main methodology that can be used, is the addition of

industrial waste materials to asphalt mixes in order to improve its resistance to

disintegration (performance) using cantabro test. The objective of this study is to

investigate the resistance to disintegration (using cantabro test) of asphahic concrete

mixes containing some industrial wastes subjected to dynamic impactloading. Selecting

two types of industrial waste material were used in this investigation, tliese are iron

blast furnace slag (IBFS) and steel brash at varied percent. Five types of mixes were

employed in this investigation: Traditional mixes, traditional mixes with IBFS by

percent 25% and 50% as coarse aggregate, traditional mixes with 4% and 6% steel

brash as filler using 60/70 penetration grade asphalt cement.

Marshall design method was used to optimise the asphalt content. Also, tlie loss

of stability and cantabro test are performed.

The results indicate the benefits that can be obtained from using IBFS and steel

brash as industrial wastes product in terms of resistance to disintegration, also, these

wastes improved the engineering properties for asphalt concrate mixes without

adversely effecting the stability and Marshall stiffness